Developed in the United States with the aim of conserving nickel resources and improving cost-effectiveness, this nickel-saving stainless steel contains reduced nickel content compared to traditional grades like 304, while incorporating a small amount of copper (Cu). Its performance is similar to 304, maintaining excellent corrosion resistance and stainless properties, and it can meet the various requirements typically placed on stainless Сталь . Цей матеріал підходить для виготовлення таблиця класу I .
Порівняння між 204cu та 304 матеріалами
Compared to 304, 204Cu has higher tensile strength and yield strength, lower cold working hardening rate, better cold forming performance, and the inherent wear resistance of 200 series steels. 204Cu has unique resistance to H₂SO₄ corrosion, superior resistance to HC₁ and HNO₃ corrosion compared to 304, but inferior high-temperature oxidation resistance compared to 304. It is not Підходить для використання у високотемпературних (більше або дорівнює 400 градусів) окислюючих середовищ .
| Матеріали | C | Сина | Мн | P | S | Ні | Cr | N | Куточок |
| 304 | Менше або дорівнює 0,08 | Менше або дорівнює 1,00 | Менше або дорівнює 2,00 | Менше або дорівнює 0,045 | Менше або дорівнює 0,03 | 8.00-10.00 | 18.00-20.00 | ||
| 204CU | Менше або дорівнює 0,10 | Менше або дорівнює 1,00 | 8.00-10.00 | Менше або дорівнює 0,06 | Менше або дорівнює 0,03 | 1.00-3.00 | 1.00-3.00 | Менше або дорівнює 0,25 | Менше або дорівнює 2,00 |
| Матеріали | Міцність виходу (MPA) | Сила на розрив (MPA) | Подовження (%) | Твердість (HV) |
| 304 | Більше або дорівнює 205 | Більше або дорівнює 515 | Більше або дорівнює 40 | Менше або дорівнює 200 |
| 204CU | Більше або дорівнює 300 | Більше або дорівнює 700 | Більше або дорівнює 55 | Менше або дорівнює 210 |